1. RROD was caused by lead free solder cracking after repeated heating and cooling cycles. Nothing whatsoever todo with cheap parts.
|
"Microsoft has never officially released any information indicating the true cause of the problem. Therefore, any information available to the public has come only from speculation and third party analysis.
Electronics industry newspaper EE Times reported that the problems may have started in the graphics chip. Microsoft designed the chip in-house to cut out the traditional ASIC vendor with the goal of saving money in ASIC design costs. After multiple product failures, Microsoft went back to an ASIC vendor and had the chip redesigned so it would dissipate less heat.[34][35]
German computer magazine c't blamed the problem primarily on the use of the wrong type of lead-free solder, a type that when exposed to elevated temperatures for extended periods of time becomes brittle and can develop hair-line cracks that are almost irreparable.[36] The article also revealed that representatives of the three largest Xbox 360 resellers in the world (EB Games, Gamestop and Best Buy) claimed that the failure rate of the Xbox 360 was between 30% and 33%, and that Micromart, the largest repair shop in the United Kingdom, stopped repairing Xbox 360s because it was unable to fully repair the defective systems. Because of the nature of the problem, Micromart could only make temporary repairs, which led to many of the "repaired" systems failing again after a few weeks. At that time Micromart was receiving 2,500 defective consoles per day from the U.K. alone."
http://en.wikipedia.org/wiki/Xbox_360_technical_problems
|
Wikipedia can say what it likes. I repair RROD Xbox 360s and can tell you straight it's always down to the solder. Everyone who repairs Xbox 360s knows this, you've heard of "reballing" right. It's a solder term and term that goes hand in hand with the Xbox 360. Basically the console PCB bends due to heating and cooling down, solder cracks. End of strory.
It's not speculation.